4.4 Suggesting Firing Schedules

Kiln Temperature

Even though the green ware looks completely dry, the body might conceal some moisture inside. The beginning of firing should be slow in a low heat for several hours. Door should be left ajar and peepholes left open to let the moisture released.

Normally for Bisque Firing, you don't want to go more than 100C/hour below 600C. Depend on the thickness of pieces, large or heavy works should have a longer soaking time between 50C -100C to avoid hidden moisture and air pockets exploded.  In these cases, it might need at 1-3 hours or longer on slow speed firing to 100c and additional soaking hours to release moisture. Thinner pieces like slip-casting ware with even thickness can follow the normal firing 100C/hour after completely bone dry. As soon as reach the 600C, it can go 150C/hour until you reach the mature temperture.

For Glaze Firing(Oxidation), it could mantian 100C/hour until 600C as long as the pieces are already biques. Then, 150C/hour or full power is on to finish up. Additional soaking 30 minture is recommanded for glaze develoment.

Firing   Bisque (Thin) Bisque (Thicker) Glaze
    Cone 010 Cone 010 Cone 6
Segment 1 Target 90C 90C  600C
  Ramp 90C/ hour 50C/ hour 100C/ hour
  Soak 0.5 hour 3 hours or above -----
  Lid Open Open -----
         
Segment 2 Target  600C 600C 1250C
  Ramp 100C/ hour 100C/ hour 150C/ hour
  Soak 0.5 hour 0.5 hour or above 0.5 hour
  Lid Close @300C Close @300C -----
        Done
         
Segment 3 Target  900C (cone 010)  900C (cone 010)  
  Ramp 150C/ hour 150C/ hour  
    Done Done